Technical Data of 50% Alumina



JAY AL - 50% is 50% Alumina Brick based on calcined bauxite of Rotary Kiln with good thermal spalling resistance, low porosity and excellent mechanical strength, Applications includes Cement Rotary Kilns, Reheat Furnaces, Metallurgical Furnaces, Boiler Furnaces, Rosting Kilns, Linings for general purpose use in steel plants including Tundish Lining and Ceramic Kilns. 

 
Chemical Analysis
  Alumina Al2O3   48.0 - 53.0 %
  Silica SiO2   38.0 - 42.0 %
  Ferric - Oxide Fe2O3   2.50 - 3.10 %
  Titanium TiO2   2.90 - 3.50 %
  Calcia Ca O   1.00 - 1.50 %
 

Physical Properties

  Pyrometric Cone Equivalent, Orton   Min. 33(1743°C)
  Reheat change - at 1400°C - 2Hrs,   Max. (+/-)0.5%
  Refractories under Load - ta Value   Min. 1400°C
  Apparent Porosity,   17.0 - 20.0%
  Bulk Density, gm/cm3   2.30 - 2.50
  Cold Crushing, Strength, kg/cm²   400 - 600
  Thermal Conductivity, W/Mok at 700°C   1.70
  Thermal Conductivity, W/Mok at 900°C   1.60
 
IMPORTANT NOTE :-
THE ABOVE TEST DATA are based on average results of Control tests on dry pressed standard size bricks and are subject to normal variation on individual tests, hence these results should not be regarded as absolute limits.
 